The porous anode cermet is a blend of nickel oxide and yttria stabilized zirconia (YSZ)tape form. It provides the catalytic activity required to promote the reaction necessary produce fuel ions, such as hydrogen or CO. It is porous so that fuel gas can reach three-phase boundary present near the electrolyte. In SOFC anode-supported cells,anode layers are required to provide mechanical strength for the cell. It is preparedtape casting a slurry containing the YSZ powder, a thermoplastic binder and surfactant. The slurry is cast on a polyester carrier film which is coated with a release agent.
Specification Information
• Sofc • Category • Laminating • Green Tape Thickness • Green Tape Density • Typical Sintering Cycle • • • Fired Shrinkage (3 layers using lamination • • Fired Density (1450 ºC for 120 minutes) • Unit Size
• Tape • 1 • 21 MPa at 70 ºC • nominal 180 µm • nominal 3.2 g/cm³, depending on solids loading • 0.7 ºC/minute ramp to 650 ºC • 2-1/2 ºC/minute ramp to 1450 to 1550 ºC • 2-hour soak at peak temperature to achieve full de • X, Y: 21% • Z: 21% • < 85% of theoretical • 500 in²
H-Tech Warranty & Guarantee
H-Tech will work directly with you to address any manufacturer defects or other warranty issues in order to resolve any problem quickly and efficiently with minimum consumer effort.
• Estimated Ship Dimensions: 12" x 6" x 6" • Estimated Ship Weight: 5 lbs • Lead time: 7 days • Shipping origin: King of Prussia, United States Please contact us for pricing on this product. H-Tech's Shipping Policy
Print This Page